Warning: This module may not support sharing across sites


You are attempting to add a reference to this module that exists on another site in this group. This module may or may not support sharing across multiple sites - it doesn't explicitly state either way whether it does.

If you are sure that it does, or if your intent is to test its ability to do so, then proceed with caution and be aware that certain functionality in the module - or even the entire module - may not function correctly in this configuration.

If you are confused by this message or are working on a site that cannot tolerate any breakage, you should click Cancel and contact the DotNetNuke Support Team.


举报方式

 

收信地址: 四川省成都市武侯区人民南路四段30号中蓝晨光化工研究设计院有限公司纪委办公室     邮编:610041
举报邮箱:cgxfjb@sinochem.com
举报电话:
高建新:028-85555041、13550116432
段  蓉:028-85590219、18108086068

电绝缘硅橡胶

来源: 蓝星中蓝晨光化工研究设计院
时间:2013-11-14

特点

耐气候老化、耐臭氧;

耐电晕、耐电弧性能;

易脱模;

适用温度广;

典型应用

高压绝缘子;

避雷器;

热压模具;

典型性能

项目

单位

数值

GX568-U

GX566-U

GX561-U

GX564-U

密度(25℃)

g/cm3

1.48

1.48

1.48

1.48

拉伸强度

MPa≥

5

4.5

4.5

4

扯断伸长率

%≥

280

260

220

200

扯断永久变形

%≤

4.0

4.0

4.0

4.0

撕裂强度

KN/m≥

12

12

10

10

硬度

HA

65±5

65±5

65±5

65±5

体积电阻率

Ω.cm≥

1.0×1015

1.0×1015

1.0×1015

1.0×1015

电气强度

KV/mm≥

22.0

22.0

20.0

18.0

相对介电常数(1MHz)

3~4

3~4

3~4

3~4

介质损耗因数(1MHz)

3.0×10-2

5.0×10-2

7.0×10-2

8.0×10-2

耐漏电起痕性和电蚀损性

TMA4.5,蚀损深度≤2.5mm

阻燃性

FV-0

使用方法

将胶料在开炼机上加入过氧化物硫化剂——双二五,返炼均匀后即可用于模压成型,模压工艺条件应根据制品的规格、形状大小确定。在开炼机上加入硫化剂前,可根据需要加入各种颜料,以配制成需要的颜色,但应注意颜料加入后需薄通均匀,最好是加入颜料膏。

根据客户需求,出厂时可加入硫化剂,也可配制成客户需求的颜色。